Sifmig No 985 Copper MIG Brazing Wire – 1.0mm x 12.5Kg
The Sifmig No 985 Copper MIG Brazing Wire, with a diameter of 1.0mm and weighing 12.5Kg, is a premium wire that boasts a composition of at least 98.5% copper, complemented with deoxidizing elements. This wire is meticulously crafted for MIG welding of copper, ensuring a robust and durable bond. Its unique formulation not only guarantees optimal welding outcomes but also provides resistance to both high temperatures and corrosion. Specifically designed for joint welding of high-oxygen copper joints and materials, it is recommended for material thicknesses greater than 6mm to pre-heat the component to temperatures between 600ºC and control cooling post-welding to ensure a slow and gradual reduction in heat.
Key Features:
- High Copper Content: Contains a minimum of 98.5% copper, ensuring superior welding quality.
- Deoxidizing Elements: Infused with elements that counteract oxidation, promoting cleaner and more resilient welds.
- Temperature and Corrosion Resilience: Offers resistance against high temperatures and corrosion, ensuring the longevity of the weld.
- Specialized Welding: Specifically designed for joint welding of high-oxygen copper joints and materials.
Typical Applications:
The Sifmig No 985 Copper MIG Brazing Wire is tailored for:
- Copper Welding: Perfect for MIG welding tasks involving copper, ensuring a strong and lasting bond.
- High-Oxygen Copper Joints: Ideal for joint welding of high-oxygen copper joints and materials.
- Thick Materials: Recommended for materials with a thickness greater than 6mm, with specific pre-heating and post-welding cooling guidelines.
Welding Positions
For use in all positions.
Specifications
| Product Type | Mig Wire – Brazing |
| Part Number | WO981012 |
| Weight | 12.5 KG |
| Diameter | 1.0 mm |
| Melting Point (DegC) | 1025 |
| Ultimate Tensile Strength (U.T.S.) N/mm2 | 220 |
| Shielding Gas | Argon |
| Current Type | Direct Current (DC+) |
Typical Weld Metal Weld Composition
| Sn (Tin) | 0.85% |
| Mn (Manganese) | 0.25% |
| P (Phosphorus) | 0.01% |
| Si (Silicon) | 0.2% |
| Cu (Copper) | Bal |
Typical Mechanical Properties
| Melting Point | 1025ËšC |
| Ultimate Tensile Strength | 220 N/mm² |
| Hardness | 70 |
Material to be Welded
Used in MIG welding of copper, this wire is ideal for joint welding of high-oxygen copper joints and materials. If material thickness is >6mm, pre-heat component 600ºC< – control cooling after welding to ensure slow, gradual reduction in heat.
BS: 2901 Â C7. EN ISO 24373: Cu 1898 [CuSn1]