Sifmig No 8 Phosphor Bronze MIG Brazing Wire – 0.8 mm x 4 Kg
Sifmig No 8 is a phosphor bronze MIG brazing wire, primarily composed of copper and enriched with 7% tin. This wire is specifically designed for fusion welding of phosphor bronze castings, copper alloys, and brass. Additionally, it’s versatile enough to be used for MIG brazing on a variety of metals including ferrous, stainless, and dissimilar metals. One of its notable applications is to provide a wear-resistant layer on surfaces prone to abrasion.
Key Features:
- Phosphor Bronze Composition: Contains 7% tin, making it suitable for welding phosphor bronze castings and copper alloys.
- Versatility: Can be used for MIG brazing on various metals and for applying a bearing surface.
- Wear Resistance: Ideal for providing a wear-resistant layer on surfaces prone to abrasion.
Typical Applications:
- Fusion Welding: Suitable for phosphor bronze castings, copper alloys, and brass.
- MIG Brazing: Can be used on ferrous, stainless, and dissimilar metals.
- Surface Layering: Used to apply a wear-resistant layer on surfaces subject to abrasion.
- Crack Repair: Effective for repairing cracks in castings.
For parent metals containing trace amounts of lead (e.g., LG2), it’s recommended to apply SIFMIG 8 in stages. Between each pass, grinding is advised to remove lead that might have been drawn into the joint, thereby reducing porosity.
Specification
Sub Category | Mig Wire – Brazing |
Part Number | WO080840 |
Weight | 4 KG |
Diameter | 0.8mm |
Melting Point DegC | 900-1050 |
U.T.S. N/mm2 | 260 |
Current | DC = + |
Shielding Gas | Pure Argon, or 95/5 (5%CO2) ArCO2 |
Welding Positions
Weldable in all positions and particularly useful in hard-to-reach areas. Ensure surfaces of parent metal are cleaned thoroughly before welding.
Typical Weld Metal Composition
Sn | 7% |
Cu | Bal |
Typical Mechanical Properties
Melting Point | 900-1050°C |
Ultimate Tensile Strength | 260 N/mm² |
Hardness | 80 |
BS: 2901 C11. Â EN ISO 24373: Cu5180A [CuSn6P]