Description
Sifmig 328 MIG Brazing Wire – 0.8 mm x 12.5 Kg
The Sifmig 328 MIG Brazing Wire, with a diameter of 0.8mm and weighing 12.5 Kg, is a 92/8 aluminium bronze wire meticulously designed for welding materials of a similar composition and copper alloys. This wire is particularly suitable for MIG Brazing dissimilar metal joints and is often chosen for maintenance applications. Its composition makes it an excellent choice for creating wear-resistant surfaces that experience relatively light loads. Furthermore, it offers resistance against corrosive media, such as salt, making it a reliable choice for various applications.
Key Features:
- Aluminium Bronze Composition: Contains 92% copper and 8% aluminium, making it suitable for welding similar materials and copper alloys.
- Versatility: Ideal for MIG Brazing dissimilar metal joints and maintenance applications.
- Corrosion Resistance: Offers resistance to corrosive media, such as salt.
- Welding Positions: Can be welded in various positions and is especially useful in specific industries and applications.
- Pre-Heat Consideration: Depending on the material thickness and aluminium content, a small amount of pre-heat or warming may be required prior to brazing.
Typical Applications:
The Sifmig 328 MIG Brazing Wire is commonly used in:
- Ship Building and Offshore Industries: For structures and components that require corrosion resistance.
- Power Generation: For components that need wear resistance and durability.
- Repair and Maintenance: Especially useful for maintaining car parts, tools, and other equipment.
- Chemical Industry: For equipment and structures that come in contact with corrosive chemicals.
- Bearings and Tools: For creating wear-resistant surfaces on bearings and tools.
- Aluminium Bronze Alloys: Suitable for welding specific aluminium bronze alloys, ensuring optimal weld quality and strength.
Basic Data
Application | MIG Welding |
Sub Category | Mig Wire – Brazing |
Part Number | WO320812A |
Weight | 12.5 KG |
Diameter | 0.8mm |
Melting Point DegC | 1030 |
U.T.S. N/mm2 | 430 |
Current Amps | 40-220 |
Current DC | + |
Shielding Gas | Pure Argon (0-15 Ipm) |
Welding Positions
Suitable for use in the ship building and offshore industries, power generation, repair and maintenance, and the chemical industry.
Particularly useful in the maintenance of car parts and tools, bearings in general, and galvanized steel sheets.
Typical Metal Weld Composition
Al | 8% |
Cu | Bal |
Typical Mechanical Properties
Melting Point | 1030°C |
Ultimate Tensile Strength | 430 N/mm² |
Hardness | 85 |
Material to be Welded
Can be used on aluminium bronze alloys: CuAl8 Fe3, CuAl10 FeMn2, CuAl9 Mn9 and cast aluminium bronzes G-CuAl8, G-CuAl10Ni.
A small amount of pre-heat/warming may be required prior to brazing, depending on the material thickness and aluminium content.
Standards
EN 14640 | Cu 6100 (CuAl8) |
BS 2901 | C28 |
AWS A5.7 | ERCuAl-Al |