Devcon Stainless Steel Putty 500g – Box of 10


£794.00 ex VAT £952.80 inc VAT

Brand: Devcon
Product Model:
In Stock

  • Non-rusting
  • Bonds to ferrous and non-ferrous metals
  • NSF certified for potable water applications
  • Acceptable for use in meat and poultry plants
  • Listed under NSN stock #8030-00-268-7934
  • Open Time: 5 Minutes
  • Gap Fill: 0.0625″ – .075″



Share this product


Devcon 10271 Stainless Steel Putty (ST) – 10 x 500 g

  • Stock No: 10271/10
  • Package Size: 500g


  • Stainless Steel Putty is a steel filled epoxy putty used for rust-free maintenance and repair work.

Recommended Applications

  • Patches, repairs and rebuilds stainless steel equipment in areas where welding is not practical or possible
  • Repairs cracks, dents and breaks in equipment, machinery or castings
  • Rebuilds shafts, trays and chutes
  • Used for repairs in dairies and food processing operations and chemical plants
  • Certified for portable water applications
  • Chemically accepted for use in USDA inspected plants.

Typical Physical Properties

  • Colour Grey
  • Mix Ratio by Volume 3.7:1
  • Mix Ratio by Weight 11:1
  • % Solids by Volume 100
  • Pot life at 25oC/ mins 58
  • Specific Volume CC/Kg 447
  • Cured Shrinkage cm/cm 0.001
  • Specific Gravity 2.24
  • Temperature resistance / oC Dry 121oC
  • Coverage 894cm2/Kg @ 5mm
  • Cured Hardness / Shore D 85 D
  • Dielectric Strength KV/mm 1.2
  • Adhesive Tensile Shear / MPa 16
  • Compressive Strength MPa 58
  • Coefficient of Thermal Expansion x10-6 – 61cm/cm/oC
  • Thickness per Coat / mm As required
  • Functional Cure Time /Hours 16
  • Recoat Time /Hours 4
  • Mixed Viscosity /cps (where applicable) Putty

Chemical Resistance

  • 7 days room temperature cure (30 days) – Testing carried out 30 days immersion at 21oC
  • Ammonia Very Good Methylene Chloride Poor
  • Cutting Oil Very Good Sodium Hypochlorite 5% (Bleach) Very Good
  • Isopropyl Alcohol Poor Sodium Hydroxide 10% Very Good
  • Gasoline (Unleaded) Very Good Sulphuric Acid 10% Fair
  • Hydrochloric Acid 10% Fair Xylene Very Good
  • Methyl ethyl Ketone (MEK) Poor
  • Excellent = +/- 1% weight change
  • Very Good = +/- 1-10% weight change
  • Fair = +/- 10-20% weight change
  • Poor = > 20% weight change


Epoxies are very good in water, saturated salt solution, leaded gasoline, mineral spirits, ASTM #3 oil and propylene glycol. Epoxies are generally not recommended for long term exposure to concentrated acids and organic solvents.

Cure A 12.7mm thick section of Devcon Stainless Steel Putty will harden at 21ºC in 4 hours. The material will be fully cured in 16 hours at which time the material can be machined, drilled or painted. The actual cure time of epoxy is determined by the mass used and the room temperature at the time of repair.

Surface Preparation

  • Proper surface preparation is essential to a successful application. The following procedures should be considered:
  • All surfaces must be dry, clean and rough.
  • If surface is oily or greasy use Devcon Fast Cleaner 2000 Spray / Cleaner Blend 300 to degrease the surface.
  • Remove all paint, rust and grime from the surface by abrasive blasting or other mechanical techniques.

Aluminium repairs: Oxidation of aluminium surfaces will reduce the adhesion of an epoxy to a surface. This film must be removed before repairing the surface, by mechanical means such as grit-blasting or chemical means.

Provide a “profile” on the metal surface by roughening the surface. This should be done ideally by grit blasting (8-40 mesh grit), grinding with a coarse wheel or an abrasive disc pad. An abrasive disc may be used provided white metal is revealed. Do not ‘feather edge’ epoxy materials. Epoxy material must be ‘locked in’ by defined edges and a good 3 – 5 mil profile.

Metal that has been handling sea water or other salt solutions should be grit blasted and high pressure water blasted and left overnight to allow any salts in the metal to ‘sweat’ to the surface. Repeat blasting may be required to ‘sweat out’ all the soluble salts. A test for chloride contamination should be performed prior to any epoxy application. The maximum soluble salts left on the substrate should be no more than 40 p.p.m. (parts per million).

Chemical cleaning with Devcon Fast Cleaner 2000 Spray / Cleaner Blend 300 should follow all abrasive preparation. This will help to remove all traces of sandblasting, grit, oil, grease,  dust or other foreign substances.

Under cold working conditions, heating the repair area to 38ºC – 43º C immediately before applying any of Devcon’s Metal-filled Epoxies is recommended. This procedure dries off any moisture, contamination or solvents and assists the epoxy in achieving maximum adhesion to the substrate.

Always try to make the repair as soon as possible after cleaning the substrate, to avoid oxidation or flash rusting. If this is not practical, a general application of FL-10 Primer will keep metal surfaces from flash rusting.

Mixing Stainless Steel Putty (ST) is formulated to be a dense mix that can be applied easily to overhead and vertical surfaces without running or sagging. Add the hardener to resin and mix thoroughly on a mixing board using a spatula. Do not mix in the containers.

Application For best results, product should be kept and applied at room temperature. Stainless Steel Putty(ST) can be applied when temperatures are between 13ºC and 52ºC. Spread the putty over prepared surface with a putty knife. Press firmly to ensure maximum surface contact and avoid trapping air. To bridge large gaps or holes use fibreglass, sheet metal or wire mesh.

Shelf life & Storage

A shelf life of 3 years from date of manufacture can be expected when stored at room temperature (22ºC) in their original containers

Technical Data Sheet Revision Date: 11.11.10 No.3


For complete safety and handling information, please refer to Material Safety Data Sheets (MSDS) prior to using this product.


ITW Devcon will replace any material found to be defective. As storage, handling and application of this material is beyond our control we can accept no liability for the results obtained.


All information on this data sheet is based on laboratory testing and is not intended for design.

MSDS can be found in “DOCUMENTS” section


Q & A

There are no questions yet

Ask a question

Your question will be answered by a store representative or other customers.

This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.

Thank you for the question!

Your question has been received and will be answered soon. Please do not submit the same question again.



An error occurred when saving your question. Please report it to the website administrator. Additional information:

Add an answer

This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.

Thank you for the answer!

Your answer has been received and will be published soon. Please do not submit the same answer again.



An error occurred when saving your answer. Please report it to the website administrator. Additional information:




There are no reviews yet

Add a review
Devcon Stainless Steel Putty 500g - Box of 10 Devcon Stainless Steel Putty 500g - Box of 10
* Rating is required
Your review
* Review is required
* Name is required
Add photos or video to your review
* Please confirm that you are not a robot

You may also like…

  • Devcon Stainless Steel Putty

    Devcon Stainless Steel Putty 500 g


    £84.70 ex VAT £101.64 inc VAT